Style

UL 1979   105℃ 30V

Document No  ：WT13700A00

Size

30AWG

Established Date：2006–01–09

Standard ：UL 1979

Conductor

Size              

AWG

30

Material          

----

Silver–Coated Copper

Conductors No.   

----

7

Construction Size    

mm

0.102 ± 0.003

Stranded Diameter             

mm

0.31

Insulation

Material

----

FEP

Color        

----

Clear

Average Thickness 

mm

0.30

Diameter         

mm

0.92 ± 0.03

Braid Shield

Material          

----

Tinned–Coated Copper

Construction      

mm

16／6／0.050 ± 0.003

Coverage         

%

95

Diameter

mm

1.15 ± 0.05

Jacket

Material          

----

FEP

Color           

----

According to customer

Average Thickness 

mm

0.13

Overall Diameter

mm

1.37 ± 0.05

Marking

Non

Electrical & Physical Properties

Item              

30AWG

Rating Temp Voltage    

105℃ 30V

Conductor Resistance 

335  OHM／KM／20℃  MAX.

Insulation Resistance     

3000 MEGA OHM／KM  MIN.

Dielectric Strength     

AC  1.0  KV／Minute

Spark Test          

2.5 KV

Insulation

Unaged

Tensile Strength

2500 PSI MIN. ( 1.76 Kg／ｍ㎡)

Elongation

200% MIN.

Aged

Tensile Strength

UNAGED MIN. 75% (168HRS×232℃)

Elongation

UNAGED MIN. 75% (168HRS×232℃)

Jacket

Unaged

Tensile Strength

2500 PSI MIN. ( 1.76 Kg／ｍ㎡)

Elongation

200% MIN.

Aged

Tensile Strength

UNAGED MIN. 75% (168HRS×232℃)

Elongation

UNAGED MIN. 75% (168HRS×232℃)

Nom. Impedance    

50  ± 3 Ohms

Nom. Capacitance     

96  ± 3 pF／m

Nom. Vel. of Prop.   

69%

VSWR Test    (0 – 6 GHZ)

Less 1.3

Flame Test          

VW–1  OK

THERMAL SHOCK

LESS 1mm at 232℃/1HR

BEND RADIUS

9mm Mininum

Attenuation

(dB／1m)

1.8GHZ

2.4GHZ

2.45GHZ

5.2GHZ

5.8GHZ

6GHZ

2.20

2.60

2.60

3.90

4.30

4.30